A new strategy to characterize the extent of reaction of thermoset elastomers

A new method for determining the extent of reaction of thermoset elastomers was developed based on equilibrium swelling and dynamic mechanical analysis (DMA). The extent of reaction was defined based on the molecular weight between crosslinks (M_c) of a polymer sample in relation to M_c at the onset of gelation and at complete reaction. The molecular weight between crosslinks was measured using equilibrium swelling, whereas rheology and DMA were used to determine the exact point of gelation and reaction completion, respectively. The extent of reaction of poly(1,8-octanediol-co-citrate) at various polymerization conditions was investigated and this method was used to study the relationship between mechanical properties, molecular weight between crosslinks, and extent of reaction.