AC and DC electrical stress reliability of Piezoelectric Lead Zirconate Titanate (PZT) thin films

Keyphrases

• Lead Zirconate Titanate Thin Films 100%
• Electrical Stress 100%
• Piezoelectric Lead Zirconate Titanate 100%
• Capacitors 66%
• Accelerated Life Test 66%
• Electric Field (E-field) 33%
• Field-induced 33%
• Scanning Electron Microscopy 33%
• Piezoelectric Response 33%
• Long-term Reliability 33%
• Activation Energy 33%
• Rapid Degradation 33%
• Microcracks 33%
• Failure Mode 33%
• Delamination 33%
• Depoling 33%
• Lognormal Distribution 33%
• Transverse piezoelectric Coefficient 33%
• Graph Analysis 33%
• Voltage Acceleration 33%
• Late Failure 33%
• AC Excitation 33%
• Field Amplitude 33%
• Electric Drive 33%
• Film Electrode 33%
• Freak 33%

Engineering

• Thin Films 100%
• Piezoelectric 100%
• Titanate 100%
• Lead Zirconate 100%
• Electric Field 20%
• Piezoelectric Coefficient 20%
• Defects 20%
• Activation Energy 20%
• Assuming 20%
• Microcracking 20%
• Failure Mode 20%
• Delamination 20%
• Lognormal Distribution 20%
• Acceleration Factor 20%
• Field Amplitude 20%
• Test Experiment 20%
• Electric Drives 20%
• Freak Failure 20%

Earth and Planetary Sciences

• Thin Films 100%
• Lead Zirconate Titanate 100%
• Scanning Electron Microscopy 33%
• Activation Energy 33%
• Electric Field 33%
• Failure Mode 33%
• Delamination 33%