Al₂O₃ and CeO₂-promoted MgO sorbents for CO₂ capture at moderate temperatures

A series of Al₂O₃ and CeO₂ modified MgO sorbents was prepared and studied for CO₂ sorption at moderate temperatures. The CO₂ sorption capacity of MgO was enhanced with the addition of either Al₂O₃ or CeO₂. Over Al₂O₃-MgO sorbents, the best capacity of 24.6 mg- CO₂/g-sorbent was attained at 100 °C, which was 61% higher than that of MgO (15.3 mg-CO₂/g-sorbent). The highest capacity of 35.3 mg-CO₂/g-sorbent was obtained over the CeO₂-MgO sorbents at the optimal temperature of 200 °C. Combining with the characterization results, we conclude that the promotion effect on CO₂ sorption with the addition of Al₂O₃ and CeO₂ can be attributed to the increased surface area with reduced MgO crystallite size. Moreover, the addition of CeO₂ increased the basicity of MgO phase, resulting in more increase in the CO₂ capacity than Al₂O₃ promoter. Both the Al₂O₃-MgO and CeO₂-MgO sorbents exhibited better cyclic stability than MgO over the course of fifteen CO₂ sorption-desorption cycles. Compared to Al₂O₃, CeO₂ is more effective for promoting the CO₂ capacity of MgO. To enhance the CO₂ capacity of MgO sorbent, increasing the basicity is more effective than the increase in the surface area.