TY - JOUR
T1 - Comparison of polylactide/nano-sized calcium carbonate and polylactide/montmorillonite composites
T2 - Reinforcing effects and toughening mechanisms
AU - Jiang, Long
AU - Zhang, Jinwen
AU - Wolcott, Michael P.
PY - 2007/12/13
Y1 - 2007/12/13
N2 - Semicrystalline polylactide (PLA) exhibits high tensile strength and modulus but very low strain-at-break and toughness. In this study, PLA nanocomposites with nano-sized precipitated calcium carbonate (NPCC) and organically modified montmorillonite (MMT) clay were prepared by melt extrusion. Morphologies, tensile mechanical properties, dynamic mechanical and rheological properties, polymer-nanoparticle interactions, and toughening mechanisms of the PLA/NPCC and PLA/MMT nanocomposites were compared. MMT and NPCC showed significantly different effects on the strength, modulus and elongation of the PLA nanocomposites. Different toughening mechanisms were first elucidated for the two types of nanocomposites based on the evidence from both macroscopic and microscopic observations. Under uniaxial tension, large quantities of microvoids were created in both PLA nanocomposites. The microvoids in PLA/NPCC caused massive crazing, while in PLA/MMT they resulted in shear yielding, particularly in the nanocomposite with 2.5 wt% MMT. The MMT stacks and platelets were found to be located between the microvoids in the extended specimens and prevented them from collapsing and coalescing.
AB - Semicrystalline polylactide (PLA) exhibits high tensile strength and modulus but very low strain-at-break and toughness. In this study, PLA nanocomposites with nano-sized precipitated calcium carbonate (NPCC) and organically modified montmorillonite (MMT) clay were prepared by melt extrusion. Morphologies, tensile mechanical properties, dynamic mechanical and rheological properties, polymer-nanoparticle interactions, and toughening mechanisms of the PLA/NPCC and PLA/MMT nanocomposites were compared. MMT and NPCC showed significantly different effects on the strength, modulus and elongation of the PLA nanocomposites. Different toughening mechanisms were first elucidated for the two types of nanocomposites based on the evidence from both macroscopic and microscopic observations. Under uniaxial tension, large quantities of microvoids were created in both PLA nanocomposites. The microvoids in PLA/NPCC caused massive crazing, while in PLA/MMT they resulted in shear yielding, particularly in the nanocomposite with 2.5 wt% MMT. The MMT stacks and platelets were found to be located between the microvoids in the extended specimens and prevented them from collapsing and coalescing.
UR - http://www.scopus.com/inward/record.url?scp=36549038684&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=36549038684&partnerID=8YFLogxK
U2 - 10.1016/j.polymer.2007.11.001
DO - 10.1016/j.polymer.2007.11.001
M3 - Article
AN - SCOPUS:36549038684
SN - 0032-3861
VL - 48
SP - 7632
EP - 7644
JO - Polymer
JF - Polymer
IS - 26
ER -