Dataset of process-structure-property feature relationships for AlSi10Mg material fabricated using laser powder bed fusion additive manufacturing

This dataset reports microstructure and mechanical property features of AlSi10Mg manufactured using laser powder bed fusion over a wide range of processing conditions. Samples were fabricated with different combinations of laser power, scan speed, and hatch spacing to probe dense regimes as well as porous samples resulting from keyholing and lack of fusion. Pore and grain/sub-grain features for each processing set were quantified. Sample porosity was measured using Archimedes density measurements and X-ray computed tomography (XCT). XCT was also used to characterize the surface roughness of samples along with pore size and morphology. Electron backscatter diffraction (EBSD) was used to characterize the grain size and morphology while scanning electron microscope (SEM) imaging and was used to measure solidification cell size. Uniaxial tension tests were performed to ascertain yield and ultimate tensile strengths, elongation, and elastic modulus, and microhardness was measured using Vickers indentation.