TY - JOUR
T1 - Effect of boronization on plasma-facing graphite surfaces and its correlation with the plasma behavior in NSTX-U
AU - Bedoya, F.
AU - Allain, J. P.
AU - Scotti, F.
AU - LaBombard, B.
AU - Kaita, R.
AU - Krstic, P. S.
N1 - Publisher Copyright:
© 2018
PY - 2018/12
Y1 - 2018/12
N2 - Boronization is a Plasma Facing Component (PFC) conditioning technique widely used in tokamak machines. The National Spherical Torus Experiment-Upgrade (NSTX-U) applied this conditioning, using a plasma glow with a deuterated Trimethyl-boron (d-TMB) and He mixture. The use of boronization during the campaign improved the plasma performance, allowing longer plasma discharges and H-mode access. The chemical state of an ATJ graphite sample, used as a proxy for the NSTX-U PFCs, was monitored in-situ using the Materials Analysis Particle Probe (MAPP) diagnostic and X-ray Photoelectron Spectroscopy (XPS). The XPS data showed a progressive rise (from < 5% to 23%) in the oxygen concentration of the boronized ATJ sample as the D+ fluence increased. Filterscopes were used to measure the light emitted by oxygen impurities in the plasma near the surface of the PFC. An increase in the registered magnitude of the OII line, normalized to the Dγ intensity, was observed as the concentration of O on the ATJ surface increased. The plasma performance was found to be strongly correlated to oxygen impurity concentrations at the plasma edge and on the PFC surface, as measured by the discharge length and access to the H-mode regime. In this work, we present a quantitative analysis of the evolution of the chemistry of the ATJ surface, and the oxygen presence in the plasma-material interface, and report relevant plasma parameters observed during the same period of time.
AB - Boronization is a Plasma Facing Component (PFC) conditioning technique widely used in tokamak machines. The National Spherical Torus Experiment-Upgrade (NSTX-U) applied this conditioning, using a plasma glow with a deuterated Trimethyl-boron (d-TMB) and He mixture. The use of boronization during the campaign improved the plasma performance, allowing longer plasma discharges and H-mode access. The chemical state of an ATJ graphite sample, used as a proxy for the NSTX-U PFCs, was monitored in-situ using the Materials Analysis Particle Probe (MAPP) diagnostic and X-ray Photoelectron Spectroscopy (XPS). The XPS data showed a progressive rise (from < 5% to 23%) in the oxygen concentration of the boronized ATJ sample as the D+ fluence increased. Filterscopes were used to measure the light emitted by oxygen impurities in the plasma near the surface of the PFC. An increase in the registered magnitude of the OII line, normalized to the Dγ intensity, was observed as the concentration of O on the ATJ surface increased. The plasma performance was found to be strongly correlated to oxygen impurity concentrations at the plasma edge and on the PFC surface, as measured by the discharge length and access to the H-mode regime. In this work, we present a quantitative analysis of the evolution of the chemistry of the ATJ surface, and the oxygen presence in the plasma-material interface, and report relevant plasma parameters observed during the same period of time.
UR - http://www.scopus.com/inward/record.url?scp=85056588605&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=85056588605&partnerID=8YFLogxK
U2 - 10.1016/j.nme.2018.10.010
DO - 10.1016/j.nme.2018.10.010
M3 - Article
AN - SCOPUS:85056588605
SN - 2352-1791
VL - 17
SP - 211
EP - 216
JO - Nuclear Materials and Energy
JF - Nuclear Materials and Energy
ER -