Effect of Soluble Corrosion Products on Electrical Double Layer in LiCl-KCl Molten Salts

Corrosion in molten salts greatly hampers the application for renewable energy applications like molten salt reactors. To develop effective strategies for corrosion mitigation, understanding the interfacial structures and properties such as specific ion adsorption and electrical double layer capacitance are crucial. Using cyclic voltammetry and electrochemical impedance spectroscopy, we systematically studied the interfaces on various model electrodes including W (solid), Bi (liquid), and the stainless steel 316 in LiCl-KCl eutectic molten salts with the addition of corrosion species CrCl₂ and FeCl₂. Both Cr²⁺ and Fe²⁺ ions increased electrical double layer capacitance, with Cr²⁺ showing specific adsorption behavior and shifting the potential of zero charge, while Fe²⁺ had minimal effect on point of zero charge. Two-working electrode measurements revealed increasing open-circuit potential and electrical double layer capacitance during the exposure of stainless steel 316, indicating its progressive corrosion and ion accumulation at the interface. X-ray photoelectron spectroscopy and Raman confirmed Cr enrichment at the interface. This work highlights the strong correlation between electrical double layer behavior and corrosion dynamics in molten salts and suggests electrical double layer capacitance as a sensitive, in situ indicator for corrosion monitoring.