Effects of acid leaching treatment of soda-lime silicate glass on crack initiation and fracture

Keyphrases

• Crack Initiation 100%
• Acid Leaching 100%
• Soda-lime-silica Glass 100%
• Crack Fracture 100%
• Annealing 66%
• Humidity 33%
• Mechanical Strength 33%
• Surface Chemistry 33%
• Residual Stress 33%
• Surface Treatment 33%
• Glass Surface 33%
• Transport Kinetics 33%
• Acid Soaking 33%
• Existing Knowledge 33%
• Fracture Stress 33%
• Failure Stress 33%
• Humid Environment 33%
• Bending Test 33%
• Molecular Water 33%
• Hertzian Indentation 33%
• Crack Initiation Stress 33%
• Dry Environment 33%
• Water Soaking 33%
• Fracture Resistance 33%
• Biaxial Bending 33%
• Crack Resistance 33%

Engineering

• Crack Initiation 100%
• Indentation 50%
• Residual Stress 50%
• Failure Stress 50%
• Glass Surface 50%
• Humid Environment 50%
• Bending Tests 50%
• Experimental Report 50%
• Crack Resistance 50%
• Dry Environment 50%
• Biaxial Bending 50%
• Fracture Resistance 50%

Material Science

• Crack Initiation 100%
• Silicate Glass 100%
• Indentation 16%
• Residual Stress 16%
• Fracture Toughness 16%
• Silicate 16%
• Surface Treatment 16%