Effects of shielding gas and spot reduction on humping suppression in high-speed laser welding

High-speed laser welding is a crucial process to enhance the production rate of fuel cell fabrication. However, exceeding a critical welding speed leads to defect formation such as humps and root concavities, which degrade weld quality and mechanical performance. This study employed shielding gas and spot reduction approaches to suppress these defects. The relationships between individual defect types and their influence on weld strength were systematically examined. Moreover, in situ high-speed synchrotron X-ray imaging was employed to comprehend the mechanisms of humping mitigation by shielding gas through analysis of instantaneous keyhole and melt pool dynamics. The observations reveal that shielding gas mitigates humping by shortening the molten pool through enhanced surface heat convection and by altering surface tension to prevent melt flow collisions. The effects of shielding gas and spot reduction were further incorporated into the dimensionless humping index (π_h) that describes the humping formation tendency. These findings provide mechanistic insights and quantitative guidance for defect control strategies in high-speed laser welding.