High capacity magnetic mesoporous carbon-cobalt composite adsorbents for removal of methylene green from aqueous solutions

Mingzhi Dai, Bryan D. Vogt

Research output: Contribution to journalArticlepeer-review

27 Scopus citations

Abstract

Mesoporous carbons containing cobalt nanoparticles are synthesized by tri-or quad-constituent self assembly of Pluronic F127, phenol-formaldehyde oligomer (resol), cobalt acetylacetonate (acac), and optionally tetraethyl orthosilicate (TEOS, optional). Upon pyrolysis in N 2 atmosphere, the resol provides sufficient carbon yield to maintain the ordered structure, while decomposition of the Co(acac) yields cobalt nanoparticles. To provide increased surface area, the dispersed silicate from condensation of TEOS can be etched after carbonization to yield micropores, Without silica templated micropores, the surface area decreases as the cobalt content increases, but there is a concurrent increase in the volume-average pore diameter (BHJ) and a dramatic increase in the adsorption capacity of methylene green with the equilibrium adsorption capacity from 2 to 90mg/g with increasing Co content. Moreover, the surface area and pore size of mesoporous composites can be dramatically increased by addition of TEOS and subsequent etching. These composites exhibit extremely high adsorption capacity up to 1151mg/g, which also increases with increases in the Co content. Additionally, the inclusion of cobalt nanoparticles provides magnetic separation from aqueous suspension. The in situ synthesis of the Co nanoparticles yields to a carbon shell that can partially protect the Co from leaching in acidic media; after 96h in 2M HCl, the powders remain magnetic.

Original languageEnglish (US)
Pages (from-to)127-134
Number of pages8
JournalJournal of Colloid And Interface Science
Volume387
Issue number1
DOIs
StatePublished - Dec 1 2012

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Biomaterials
  • Surfaces, Coatings and Films
  • Colloid and Surface Chemistry

Fingerprint

Dive into the research topics of 'High capacity magnetic mesoporous carbon-cobalt composite adsorbents for removal of methylene green from aqueous solutions'. Together they form a unique fingerprint.

Cite this