T1 - Joining aluminium to titanium by MIG welding-brazing process
AU - Chen, Bo
AU - Zhang, Hongtao
AU - Zhou, Jun
AU - Jiang, Wenjie
PY - 2011
Y1 - 2011
N2 - With Al-Si welding wire ER4043, lap joint between aluminium and titanium alloy was made by MIG welding-brazing process with nocolok flux aiding filler metal in promoting metal wettability. A thin intermetallic compound layer was formed at the interface between the weld metal and titanium alloy and the layer mainly consits of TiAl3 phase. The tensile strength of the joint can reach 151MPa and fracture occurred in aluminium base metal.
AB - With Al-Si welding wire ER4043, lap joint between aluminium and titanium alloy was made by MIG welding-brazing process with nocolok flux aiding filler metal in promoting metal wettability. A thin intermetallic compound layer was formed at the interface between the weld metal and titanium alloy and the layer mainly consits of TiAl3 phase. The tensile strength of the joint can reach 151MPa and fracture occurred in aluminium base metal.
UR - http://www.scopus.com/inward/record.url?scp=79960778344&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=79960778344&partnerID=8YFLogxK
U2 - 10.4028/www.scientific.net/AMR.284-286.165
DO - 10.4028/www.scientific.net/AMR.284-286.165
M3 - Conference contribution
AN - SCOPUS:79960778344
SN - 9783037851913
T3 - Advanced Materials Research
SP - 165
EP - 168
BT - Materials and Design
T2 - 2011 International Conference on Advanced Engineering Materials and Technology, AEMT 2011
Y2 - 29 July 2011 through 31 July 2011
ER -