Morphological forms of α-alumina particles synthesized in 1,4-butanediol solution

Phase-pure, monodispersed, hexagonal plates of single-crystal α-alumina (≈2 μm wide and ≈0.5 μm thick) have been prepared via precipitation by treating an aluminum hydrous oxide precursor in 1,4-butanediol at 300°C under autogenous vapor pressure. Present work shows that KOH is the only reagent that precipitates an aluminum hydrous oxide precursor suitable to synthesize °-alumina in 1,4-butanediol solution. In contrast, the use of NaOH or NH₄OH as the precipitating reagent for the precursor material does not yield the alpha phase. The solution pH at which the precursor materials are precipitated is also a critical factor for the formation of α-Al₂O₃. Phase-pure α-alumina powders were also only synthesized from the aluminum hydrous oxide precursors precipitated in the pH range from 10 to 10.5. The results of X-ray diffraction and scanning electron microscopy indicate that longer reaction times promote the phase transformation from the intermediate boehmite phase to α-alumina. The complete transformation from boehmite to α-alumina requires reaction times of about 12 h.