TY - JOUR
T1 - On the Bonding Mechanism in Cold Spray of Deformable hex-BN-Ni Clusters
AU - Neshastehriz, M.
AU - Smid, I.
AU - Segall, A. E.
AU - Eden, T. J.
N1 - Publisher Copyright:
© 2016, ASM International.
PY - 2016/6/1
Y1 - 2016/6/1
N2 - Bond strength and the lubrication potential of coatings made of 7 µm Hexagonal Boron Nitride particles encapsulated with nickel (hBN-Ni), and deposited onto aluminum 6061 substrates via cold spray were examined; for all tests, N2 was used as the carrier gas at a temperature of 480 °C and pressure of 2.4 MPa. Results showed significant improvement in both wear resistance and reduced surface friction. Coated samples also demonstrated unexpected high bond strength, which was much greater than pure nickel cold sprayed onto aluminum. However, while the results were truly promising, the primary reason for the observed high bond strength could not be explained using existing cold spray theories which were primarily developed for pure metal particles. Based on the present findings compared to cold-sprayed layers of composite nickel-nickel (nickel particles encapsulated with nickel), a mechanism for bonding of hBN-Ni particles to aluminum based on the level of plastic deformation and hardenability is proposed. Indeed, the high bond strength between the coating and substrate is related to the relatively high initial ductility of the nickel encapsulation, compliance of the hBN, as well as the ensuing significant plastic deformation of the composite particles during cold spray deposition.
AB - Bond strength and the lubrication potential of coatings made of 7 µm Hexagonal Boron Nitride particles encapsulated with nickel (hBN-Ni), and deposited onto aluminum 6061 substrates via cold spray were examined; for all tests, N2 was used as the carrier gas at a temperature of 480 °C and pressure of 2.4 MPa. Results showed significant improvement in both wear resistance and reduced surface friction. Coated samples also demonstrated unexpected high bond strength, which was much greater than pure nickel cold sprayed onto aluminum. However, while the results were truly promising, the primary reason for the observed high bond strength could not be explained using existing cold spray theories which were primarily developed for pure metal particles. Based on the present findings compared to cold-sprayed layers of composite nickel-nickel (nickel particles encapsulated with nickel), a mechanism for bonding of hBN-Ni particles to aluminum based on the level of plastic deformation and hardenability is proposed. Indeed, the high bond strength between the coating and substrate is related to the relatively high initial ductility of the nickel encapsulation, compliance of the hBN, as well as the ensuing significant plastic deformation of the composite particles during cold spray deposition.
UR - http://www.scopus.com/inward/record.url?scp=84968563080&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=84968563080&partnerID=8YFLogxK
U2 - 10.1007/s11666-016-0416-6
DO - 10.1007/s11666-016-0416-6
M3 - Article
AN - SCOPUS:84968563080
SN - 1059-9630
VL - 25
SP - 982
EP - 991
JO - Journal of Thermal Spray Technology
JF - Journal of Thermal Spray Technology
IS - 5
ER -