Proton irradiation-decelerated intergranular corrosion of Ni-Cr alloys in molten salt

Weiyue Zhou, Yang Yang, Guiqiu Zheng, Kevin B. Woller, Peter W. Stahle, Andrew M. Minor, Michael P. Short

Research output: Contribution to journalArticlepeer-review

50 Citations (SciVal)


The effects of ionizing radiation on materials often reduce to “bad news”. Radiation damage usually leads to detrimental effects such as embrittlement, accelerated creep, phase instability, and radiation-altered corrosion. Here we report that proton irradiation decelerates intergranular corrosion of Ni-Cr alloys in molten fluoride salt at 650 °C. We demonstrate this by showing that the depth of intergranular voids resulting from Cr leaching into the salt is reduced by proton irradiation alone. Interstitial defects generated from irradiation enhance diffusion, more rapidly replenishing corrosion-injected vacancies with alloy constituents, thus playing the crucial role in decelerating corrosion. Our results show that irradiation can have a positive impact on materials performance, challenging our view that radiation damage usually results in negative effects.

Original languageEnglish (US)
Article number3430
JournalNature communications
Issue number1
StatePublished - Dec 1 2020

All Science Journal Classification (ASJC) codes

  • General Chemistry
  • General Biochemistry, Genetics and Molecular Biology
  • General Physics and Astronomy


Dive into the research topics of 'Proton irradiation-decelerated intergranular corrosion of Ni-Cr alloys in molten salt'. Together they form a unique fingerprint.

Cite this